HOME > Products > Electronic material > Aluminum PWB material > AC-7210N
Aluminum base PWB material / High thermal conductive type
|
λ=8W/mK / Tg=300℃
|
AC-7210N |
|
■Composition |
|
|
■Standard specification |
| Items |
Specifications |
Tickness of insulation layer
(μm) |
120 |
Thickness of Cu foil
(μm) |
35 / 70 / 105 |
Thickness of Aluminum plate
(mm) |
1.0 / 1.5 / 2.0 |
Shipping size
(mm) |
510mm × 510mm
340mm × 510mm
and so on |
|
■Applications |
|
Power LED substrate
Power device substrate
Replacement of thermal paste
|
■Breakdown voltage |
|
Insulation layer of 0.12mm thickness can withstand voltage of 5000V. |
■Hot breakdown voltage |
|
AC-7210N can withstand voltage of 5000V even under hot temperature as shown the above. |
■Peel strength after long term heat treatment |
 |
| Peel strength hardly decreased even after 3000-hour of heat treatment at 175℃ or 200℃ |
■General properties |
| Test items |
Unit |
Treatment |
AC-7210N |
Remarks |
| Thermal conductivity |
TIM tester method |
W/m･K |
A |
8 |
Insulation layer |
| Glass transition temperature |
DMA |
℃ |
A |
300< |
Coefficient of thermal expansion
(Z-direction) |
α1 |
ppm/℃ |
A |
10～30 |
| α2 |
40～80 |
| UL flammability |
- |
UL94 |
V-0
equiv. |
| Thermal conductivity |
TIM tester method |
W/m･K |
A |
8 |
Aluminum base
PWB material |
| Breakdown voltage |
120μm
(insulation layer) |
kV |
A |
5 |
| Solder limit |
280℃
Float |
sec |
A |
300< |
| Peel strength |
35μｍ |
kN/m |
A |
1.2 |
|
| The above figures are not guaranteed value but one of the test results at our laboratories. |
■RISHO's proposal |
| We propose that substrate for mounting power LEDs could be made with AD-7210N (bonding sheet) without using ceramic substrate. |
▲AD-7210N
(Bonding sheet) |
▲Composition |
▼Images of our proposal |
 |
▲Image of power LED substrate made of ceramic
|
 |
▲Image of power LED substrate made with AD-7210N |