HOME > Products > Insulating material / Industrial plastic > Thermosetting resin laminates /Line-ups
> Paper/Phenolic laminates (Thick plate)
Paper/Phenolic laminates (Thick plate)
▲PS-1111E |
▲PS-1122E |
▲PS-1152F |
Application:
Insulating plate or mechanical parts for switchboard breaker,transformer or railcar
| Test items |
Unit |
PS-1111E |
PS-1122E |
PS-1152F |
| JIS/ANSI |
|
PL-PEV
/XXX equiv. |
-
/XX equiv. |
-/- |
| Color |
Natural |
Black |
Brown |
Electrical strength
(Vertical to layer) |
In oil 1 min. |
MV/m |
16 OK
(16<) |
15 OK
(13<) |
15 OK |
Breakdown voltage
(Vertical to layer) |
In oil 1 min. |
MV/m |
30～45 |
30～45 |
20～27 |
Electrical strength
(Parallel to layer) |
In hot oil |
kV |
8 OK
(8 <) |
8 OK
(8 <) |
- |
Breakdown voltage
(Parallel to layer) |
In hot oil |
kV |
15～25 |
15～25 |
- |
| Insulation resistance |
at RT |
MΩ |
104～105
(5×103<) |
104～105
(5×102<) |
104～105 |
| After heat treatment |
1×102～5×103
(5×10<) |
10～102
(10<) |
102～103 |
| Volume resistivity |
at RT |
MΩ-cm |
106～107 |
106～107 |
- |
| After moisture treatment |
|
|
|
| Surface resistance |
at RT |
MΩ |
104～105 |
104～105 |
- |
| After moisture treatment |
|
|
|
Dielectric constant
(1MHz) |
at RT |
- |
4.5～5.5 |
4.5～5.5 |
4.5～5.5 |
| After dipping treatment |
|
|
|
Dissipation factor
(1MHz) |
at RT |
- |
0.035～0.055 |
0.035～0.055 |
0.040～0.060 |
| After dipping treatment |
|
|
|
| Flexural strength |
Vertical to layer |
MPa |
105～180
(88<) |
105～195
(98<) |
85～130 |
| Parallel to layer |
140～190 |
140～190 |
75～130 |
| Compressive strength |
Vertical to layer |
MPa |
245～300 |
245～300 |
145～245 |
| Parallel to layer |
145～200 |
145～200 |
95～200 |
| Tensile strength |
MPa |
100～150 |
100～150 |
- |
| Izod impact strength |
Parallel to layer |
J/cm |
0.29～0.39
(0.15<) |
0.29～0.39
(0.20<) |
0.20～0.39 |
| Cleavage strength |
kN |
3.9～4.9
(2.9<) |
3.9～4.9
(3.4<) |
3.4～4.9 |
| Rockwell hardness |
|
- |
M.105～115 |
M.105～115 |
M.100～110 |
| Water absorption |
1.6mm thick |
% |
|
|
|
| 3.0mm thick |
(0.95>) |
(1.30>) |
(1.30>) |
| 10mm thick |
0.2～0.4
(0.60>) |
0.2～0.4
(0.85>) |
0.2～0.4
(0.85>) |
| Appearance after heating treatment |
2 hours |
℃ |
130 OK
(130℃) |
130 OK
(130℃) |
120 OK
(120℃) |
| Specific gravity |
- |
1.34～1.40
(1.25-1.50) |
1.34～1.40
(1.25-1.50) |
1.36～1.40
(1.25-1.50) |
| Acetone resistance |
- |
OK
(OK) |
OK
(OK) |
OK |
| UL flammability |
- |
- |
- |
94V-0 equiv.
(1.6mm<) |
*The above figures show the standard properties and guaranteed value is showed in parentheses
*Test method : JIS K-6911 |
Specifications and dimension
|
PS-1111E |
PS-1122E |
PS-1152 |
| Thickness(mm) |
3～50 |
3～50 |
3～30 |
Standad dimension
(mm) |
1000×1000 |
◯ |
◯ |
◯ |
| 1000×1200 |
◯ |
◯(3～40) |
|
| 1000×1500 |
◯ |
◯ |
|
| 1000×2000 |
◯(3～40) |
◯(3～40) |
|
| 1200×2000 |
|
◯(3～40) |
|
Thickess
tolerance
(mm) |
|
|
|
|
| 0.5 |
|
|
|
| 0.6 |
|
|
|
| 0.8 |
|
|
|
| 1.0 |
|
|
|
| 1.2 |
|
|
|
| 1.5 |
|
|
|
| 1.6 |
|
|
|
| 2.0 |
|
|
|
| 2.5 |
|
|
|
| 3.0 |
±0.20 |
±0.20 |
±0.20 |
| 4.0 |
±0.25 |
±0.25 |
±0.25 |
| 5.0 |
±0.30 |
±0.30 |
±0.30 |
| 6.0 |
±0.35 |
±0.35 |
±0.35 |
| 8.0 |
±0.40 |
±0.40 |
±0.40 |
| 10.0 |
±0.45 |
±0.45 |
±0.45 |
| 12.0 |
±0.50 |
±0.50 |
±0.50 |
| 15.0 |
±0.55 |
±0.55 |
±0.55 |
| 16.0 |
±0.60 |
±0.60 |
±0.60 |
| 18.0 |
±0.70 |
±0.70 |
±0.70 |
| 20.0 |
±0.70 |
±0.70 |
±0.70 |
| 25.0 |
±0.85 |
±0.85 |
±0.85 |
| 30.0 |
±1.00 |
±1.00 |
±1.00 |
| 35.0 |
- |
- |
|
| 40.0 |
- |
- |
|
| 50.0 |
- |
- |
|
| 75.0 |
|
|
|
100.0
|
|
|
|
*Minimum quantity of order would be quoted according to product |