Paper/Phenolic laminates (Thick plate) PS-1121E(PL-PEM/XX)
| Test items |
Unit |
Treatment |
PS-1121E |
| JIS/ANSI |
PL-PEM/xx eqiiv. |
| Color |
Natural |
Electrical strength
(Vertical to layer) |
In oil 1 min. |
MV/m |
C-90/20/65 |
15 OK
(13<) |
Breakdown voltage
(Vertical to layer) |
In oil 1 min. |
MV/m |
C-90/20/65 |
30～45 |
Electrical strength
(Parallel to layer) |
In hot oil |
kV |
O-0.5/90 |
8 OK
(8 <) |
Breakdown voltage
(Parallel to layer) |
In hot oil |
kV |
O-0.5/90 |
15～25 |
| Insulation resistance |
at RT |
MΩ |
C-90/20/65 |
104～105
(5×102<) |
| After heat treatment |
C-90/20/65
+D-2/100 |
10～102
(10<) |
| Volume resistivity |
at RT |
MΩ-cm |
C-90/20/65 |
106～107 |
| After moisture treatment |
C-90/20/65
+C-96/40/90 |
|
| Surface resistance |
at RT |
MΩ |
C-90/20/65 |
104～105 |
| After moisture treatment |
C-90/20/65
+C-96/40/90 |
|
Dielectric constant
(1MHz) |
at RT |
- |
C-90/20/65 |
4.5～5.5 |
| After dipping treatment |
C-90/20/65
+D-24/23 |
|
Dissipation factor
(1MHz) |
at RT |
- |
C-90/20/65 |
0.035～0.055 |
| After dipping treatment |
C-90/20/65
+D-24/23 |
|
| Flexural strength |
Vertical to layer |
MPa |
A |
105～195
(98<) |
| Parallel to layer |
140～190 |
| Compressive strength |
Vertical to layer |
MPa |
A |
245～300 |
| Parallel to layer |
145～200 |
| Tensile strength |
MPa |
A |
100～150 |
| Izod impact strength |
Parallel to layer |
J/cm |
A |
0.29～0.39 (0.20<) |
| Cleavage strength |
kN |
A |
3.9～4.9
(3.4<) |
| Rockwell hardness |
|
- |
A |
M.105～115 |
| Water absorption |
1.6mm thick |
% |
E-24/50 +D-24/23 |
|
| 3.0mm thick |
E-24/50 +D-24/23 |
(1.30>) |
| 10mm thick |
E-24/50 +D-24/23 |
0.2～0.4
(0.85>) |
| Appearance after heating treatment |
2 hours |
℃ |
A |
130 OK
(130℃) |
| Specific gravity |
- |
A |
1.34v1.40
(1.25-1.50) |
| Acetone resistance |
- |
A |
OK
(OK) |
|
*The above figures show the standard properties and guaranteed value is
showed in parentheses
*Test method:JIS K-6911
*Treatment condition
A=Accepted state, C=Constant Temperature and humidity , D=Dipping in
water E=Electric heating, O=Oil dipping
Starting from the left figures show Time(h)/Temeperature(℃)/Humidity(%) |
Specifications and dimension
| Thickness(mm) |
3～50 |
Standad dimension
(mm) |
1000×1000 |
◯ |
| 1000×1200 |
◯(3～40) |
| 1000×1500 |
◯ |
| 1000×2000 |
◯(3～40) |
| 1200×2000 |
◯(3～40) |
Thickess
tolerance
(mm) |
|
|
| 0.5 |
|
| 0.6 |
|
| 0.8 |
|
| 1.0 |
|
| 1.2 |
|
| 1.5 |
|
| 1.6 |
|
| 2.0 |
|
| 2.5 |
|
| 3.0 |
±0.20 |
| 4.0 |
±0.25 |
| 5.0 |
±0.30 |
| 6.0 |
±0.35 |
| 8.0 |
±0.40 |
| 10.0 |
±0.45 |
| 12.0 |
±0.50 |
| 15.0 |
±0.55 |
| 16.0 |
±0.60 |
| 18.0 |
±0.70 |
| 20.0 |
±0.70 |
| 25.0 |
±0.85 |
| 30.0 |
±1.00 |
| 35.0 |
- |
| 40.0 |
- |
| 50.0 |
- |
| 75.0 |
|
100.0
|
|
|