HOME > Products > Insulating material / Industrial plastic > Thermosetting resin laminates /Line-ups
> Paper/Phenolis laminates(Thin plate)
Paper/Phenolis laminates(Thin plate)
▲PS-1131 |
▲PS-1135 |
▲PS-1131S |
Application:
punching parts such as rotary switch
| Test items |
Unit |
PS-1131 |
PS-1135 |
PS-1131S |
| JIS/ANSI |
|
PL-P-P/XPC |
PL-P-P/XPC |
PL-P-P/XPC |
| Color |
Brown |
Black |
Blown |
Electrical strength
(Vertical to layer) |
In oil 1 min. |
MV/m |
10 OK |
10 OK |
10 OK |
Breakdown voltage
(Vertical to layer) |
In oil 1 min. |
MV/m |
|
|
|
Electrical strength
(Parallel to layer) |
In hot oil |
kV |
|
|
|
Breakdown voltage
(Parallel to layer) |
In hot oil |
kV |
|
|
|
| Insulation resistance |
at RT |
MΩ |
105～106
(102<) |
105～106
(102<) |
105～106
(102<) |
| After heat treatment |
10～102 |
10～102 |
102～103 |
| Volume resistivity |
at RT |
MΩ-cm |
105～106 |
105～106 |
5×105～5×106 |
| After moisture treatment |
104～5×105 |
104～5×105 |
5×104～106 |
| Surface resistance |
at RT |
MΩ |
104～106 |
104～106 |
5×104～5×106 |
| After moisture treatment |
102～104 |
102～104 |
5×102～5×104 |
Dielectric constant
(1MHz) |
at RT |
- |
3.5～4.5 |
3.5～4.5 |
3.5～4.5 |
| After dipping treatment |
4.0～5.0 |
4.0～5.0 |
4.0～5.0 |
Dissipation factor
(1MHz) |
at RT |
- |
0.030～0.045 |
0.030～0.045 |
0.030～0.040 |
| After dipping treatment |
0.040～0.060 |
0.040～0.060 |
0.035～0.045 |
| Flexural strength |
Vertical to layer |
MPa |
100～175
(69<) |
100～175
(69<) |
120～175
(69<) |
| Parallel to layer |
|
|
|
| Compressive strength |
Vertical to layer |
MPa |
|
|
|
| Parallel to layer |
|
|
|
| Tensile strength |
MPa |
|
|
|
| Izod impact strength |
Parallel to layer |
J/cm |
|
|
|
| Cleavage strength |
kN |
|
|
|
| Rockwell hardness |
|
- |
|
|
|
| Water absorption |
1.6mm thick |
% |
1.0～1.6
(3.60>) |
1.0～1.6
(3.60>) |
0.6～1.2
(3.60>) |
| 3.0mm thick |
|
|
|
| 10mm thick |
|
|
|
| Appearance after heating treatment |
2 hours |
℃ |
120 OK
(120℃) |
120 OK
(120℃) |
120 OK
(120℃) |
| Specific gravity |
- |
1.30～1.40
(1.25-1.50) |
1.30～1.40
(1.25-1.50) |
1.30～1.40
(1.25-1.50) |
| Acetone resistance |
- |
OK
|
OK
|
OK |
| Flame resistance |
UL |
- |
94HB |
94HB |
94HB |
| Punching workability |
℃ |
at RT |
at RT |
60～90 |
|
*The above figures show the standard properties and guaranteed value is showed in parentheses
*Test method : JIS K-6911 |
Specifications and dimension
| Thickness(mm) |
0.4～3.0 |
Standad dimension
(mm) |
1000×1000 |
◯ |
| 1000×1200 |
◯ |
| 1000×1500 |
|
| 1000×2000 |
|
| 1200×2000 |
|
Thickess
tolerance
(mm) |
|
|
| 0.5 |
±0.08 |
| 0.6 |
±0.08 |
| 0.8 |
±0.10 |
| 1.0 |
±0.10 |
| 1.2 |
±0.13 |
| 1.5 |
±0.13 |
| 1.6 |
±0.15 |
| 2.0 |
±0.15 |
| 2.5 |
±0.20 |
| 3.0 |
±0.20 |
| 4.0 |
|
| 5.0 |
|
| 6.0 |
|
| 8.0 |
|
| 10.0 |
|
| 12.0 |
|
| 15.0 |
|
| 16.0 |
|
| 18.0 |
|
| 20.0 |
|
| 25.0 |
|
| 30.0 |
|
| 35.0 |
|
| 40.0 |
|
| 50.0 |
|
| 75.0 |
|
100.0
|
|
|