Paper/Phenolis laminates(Thin plate)
 |
 |
▲PS-1143S(left)
for cold punching and PS-1143L
for Hot punching |
▲Punched parts |
Application:
punching parts for such as rotary switch
| Test items |
Unit |
Treatment |
PS-1143S |
PS-1143L |
JIS
ANSI |
|
PL-PEM-P
XXP equiv. |
PL-PEM-P
XXP equiv. |
| Color |
Brown |
Brown |
Electrical strength
(Vertical to layer) |
In oil 1 min. |
MV/m |
C-90/20/65 |
12 OK |
12 OK |
Breakdown voltage
(Vertical to layer) |
In oil 1 min. |
MV/m |
C-90/20/65 |
|
|
Electrical strength
(Parallel to layer) |
In hot oil |
kV |
O-0.5/90 |
|
|
Breakdown voltage
(Parallel to layer) |
In hot oil |
kV |
O-0.5/90 |
|
|
| Insulation resistance |
at RT |
MΩ |
C-90/20/65 |
105～106
(5×102<) |
105～106
(5×102<) |
| After heat treatment |
C-90/20/65
+D-2/100 |
102～103
(5<) |
5×10～5×102
(5<) |
| Volume resistivity |
at RT |
MΩ-cm |
C-90/20/65 |
106～107 |
106～107 |
| After moisture treatment |
C-90/20/65
+C-96/40/90 |
104～106 |
104～105 |
| Surface resistance |
at RT |
MΩ |
C-90/20/65 |
104～106 |
104～106 |
| After moisture treatment |
C-90/20/65
+C-96/40/90 |
103～104 |
5×102～5×104 |
Dielectric constant
(1MHz) |
at RT |
- |
C-90/20/65 |
3.5～4.5 |
3.5～4.5 |
| After dipping treatment |
C-90/20/65
+D-24/23 |
4.0～5.0 |
4.0～5.0 |
Dissipation factor
(1MHz) |
at RT |
- |
C-90/20/65 |
0.030～0.040 |
0.030～0.040 |
| After dipping treatment |
C-90/20/65
+D-24/23 |
0.035～0.045 |
0.035～0.045 |
| Flexural strength |
Vertical to layer |
MPa |
A |
135～190
(79<) |
150～195
(79<) |
| Parallel to layer |
A |
|
|
| Compressive strength |
Vertical to layer |
MPa |
A |
|
|
| Parallel to layer |
A |
|
|
| Tensile strength |
MPa |
A |
|
|
| Izod impact strength |
Parallel to layer |
J/cm |
A |
|
|
| Cleavage strength |
kN |
A |
|
|
| Rockwell hardness |
|
- |
A |
|
|
| Water absorption |
1.6mm thick |
% |
E-24/50
+D-24/23 |
0.5～1.0
(1.80>) |
0.8～1.2
(1.80>) |
| 3.0mm thick |
E-24/50
+D-24/23 |
|
|
| 10mm thick |
E-24/50
+D-24/23 |
|
|
| Appearance after heating treatment |
2 hours |
℃ |
A |
120 OK
(120℃) |
120 OK
(120℃) |
| Specific gravity |
- |
A |
1.30～1.40
(1.25-1.50) |
1.30～1.40
(1.25-1.50) |
| Acetone resistance |
- |
A |
OK
|
OK
|
| Flame resistance |
UL |
- |
E-168/70 |
94HB
equiv. |
94HB
equiv. |
| Punching workability |
℃ |
A |
70～90 |
80～120 |
|
*The above figures show the standard properties and guaranteed value is showed in parentheses
*Test method : JIS K-6911
*Treatment condition
A=Accepted state, C=Constant Temperature and humidity , D=Dipping in water E=Electric heating , O=Oil dipping
Starting from the left figures show Time(h)/Temeperature(℃)/Humidity(%) |
Specifications and dimension
| Thickness(mm) |
0.5～2.5 |
Standad dimension
(mm) |
1000×1000 |
◯ |
| 1000×1200 |
◯ |
| 1000×1500 |
|
| 1000×2000 |
|
| 1200×2000 |
|
Thickess
tolerance
(mm) |
|
|
| 0.5 |
±0.08 |
| 0.6 |
±0.08 |
| 0.8 |
±0.10 |
| 1.0 |
±0.10 |
| 1.2 |
±0.13 |
| 1.5 |
±0.13 |
| 1.6 |
±0.15 |
| 2.0 |
±0.15 |
| 2.5 |
±0.20 |
| 3.0 |
|
| 4.0 |
|
| 5.0 |
|
| 6.0 |
|
| 8.0 |
|
| 10.0 |
|
| 12.0 |
|
| 15.0 |
|
| 16.0 |
|
| 18.0 |
|
| 20.0 |
|
| 25.0 |
|
| 30.0 |
|
| 35.0 |
|
| 40.0 |
|
| 50.0 |
|
| 75.0 |
|
100.0
|
|
|